304不锈钢硬度，用途，不锈钢硬度抗拉强度对照表
硬度，抗拉强度对照表
无锡不锈钢市场提供
| 维氏(HV) | 洛氏HRC | 洛氏HRA | 强度N/mm2 | 维氏(HV) | 洛氏RC | 洛氏RA | 强度N/mm2 | 维氏(HV) | 洛氏RC | 洛氏RA | 强度N/mm2 | ||
| 625 | 57 | 79.5 | 2315 | 400 | 42 | 71.7 | 1350 | 260 | 26 | 63.3 | 895 | ||
| 605 | 56 | 78.9 | 2210 | 389 | 41 | 71.7 | 1310 | 254 | 25 | 62.8 | 875 | ||
| 587 | 55 | 78.4 | 2115 | 378 | 40 | 70.6 | 1275 | 247 | 24 | 62.3 | 845 | ||
| 569 | 54 | 77.9 | 2030 | 368 | 39 | 70.1 | 1235 | 241 | 23 | 61.7 | 825 | ||
| 551 | 53 | 77.4 | 1945 | 358 | 38 | 69.6 | 1200 | 235 | 22 | 61.2 | 805 | ||
| 535 | 52 | 76.9 | 1875 | 348 | 37 | 69 | 1170 | 229 | 21 | 60.7 | 790 | ||
| 520 | 51 | 76.3 | 1805 | 339 | 36 | 68.5 | 1140 | 224 | 20 | 60.2 | 770 | ||
| 504 | 50 | 75.8 | 1750 | 329 | 35 | 68 | 1115 | 218 | 19 | 59.7 | 755 | ||
| 489 | 49 | 75.3 | 1680 | 321 | 34 | 67.5 | 1085 | 213 | 18 | 59.1 | 739 | ||
| 475 | 48 | 74.8 | 1620 | 312 | 33 | 67 | 1060 | 208 | 17 | 58.6 | 724 | ||
| 461 | 47 | 74.2 | 1580 | 304 | 32 | 66.4 | 1030 | 203 | 16 | 58.1 | 710 | ||
| 443 | 46 | 73.7 | 1530 | 289 | 30 | 65.4 | 985 | 198 | 15 | 57.6 | 690 | ||
| 435 | 45 | 73.2 | 1480 | 281 | 29 | 64.9 | 950 | 193 | 14 | 57.1 | 677 | ||
| 423 | 44 | 72.7 | 1440 | 274 | 28 | 64.4 | 950 | 189 | 13 | 56.5 | 662 | ||
| 411 | 43 | 72.2 | 1390 | 267 | 27 | 62.8 | 915 | 180 | 11 | 55.5 | 625 |
名词解释：布氏硬度(HB)，洛氏硬度(HR)，维氏硬度(HV)
⑴布氏硬度(HB)
以一定的载荷(一般3000kg)把一定大小(直径一般为10mm)的淬硬钢球压入材料表面，保持一段时间，去载后，负荷与其压痕面积之比值，即为布氏硬度值(HB)
，单位为公斤力/mm2 (N/mm2)。
⑵洛氏硬度(HR)
当HB>450或者试样过小时，不能采用布氏硬度试验而改用洛氏硬度计量。它是用一个顶角120°的金刚石圆锥体或直径为1.59、3.18mm的钢球，在一定载荷下压
入被测材料表面，由压痕的深度求出材料的硬度。根据试验材料硬度的不同，分三种不同的标度来表示：
HRA：是采用60kg载荷和钻石锥压入器求得的硬度，用于硬度极高的材料(如硬质合金等)。
HRB：是采用100kg载荷和直径1.58mm淬硬的钢球，求得的硬度，用于硬度较低的材料(如退火钢、铸铁等)。
HRC：是采用150kg载荷和钻石锥压入器求得的硬度，用于硬度很高的材料(如淬火钢等)。
⑶维氏硬度(HV)
以120kg以内的载荷和顶角为136°的金刚石方形锥压入器压入材料表面，用材料压痕凹坑的表面积除以载荷值，即为维氏硬度值(HV)